Printing PS version of the base method for producing aluminum sheet, characterized in that it is the method steps:
A. according to the parts by weight ratio of Al: 98, Si: <1.0, Fe: 0.3 ~ 1.0, Cu: 0.03, Zn: 0.03, Mg: 0.03, Ti: 0.05 ratio will be above the melting temperature of the alloy composition after mixing 720 - under the conditions of 800 ℃ melting;
B. then for the next casting temperature condition of 690 ~ 750 ℃ alloy casting into ingot;
C. alloy ingot to make the ingot at a temperature of 500 ~ 610 ℃ conditions homogenization;
D. then subjected to hot rolling at a temperature of 400 ~ 540 ℃ temperature;
E. hot-rolled material consisting of 9.0mm cold-rolled to 0.7mm;
F. at a temperature of 300 ℃ ~ 500 ℃ conditions of intermediate annealing 11h, insulation 1h then cold rolling to 0.15mm, stretched, fully straightening, after cutting to be finished.
PS Base with Aluminum Fabrication Steps
Aluminium Sheets
View DetailsAluminium Coils
View DetailsAluminium Foils
View DetailsAluminium Strips
View DetailsAluminium Circles
View DetailsCoated Aluminium
View DetailsMirror Aluminum
View DetailsStucco Embossed Aluminum
View DetailsAluminum
- 2A17 aluminum round bar rod
- Aluminum Foil Products Stock (...
- 5052 Aluminum Alloy Sheet
- Production and construction of...
- 7150 T7751 Aluminum Block plat...
- Aluminum foil tape for PPR Pi...
- 2017-T4/T451 Aluminum Sheet
- 2124 aluminum blocks
- aluminum profile photo frame
- Omnia Jar Aluminum Cap Strip F...
- 1060 H18 Color Coated Roller S...
- Why do aluminum alloys need to...
- PVDF Coated Aluminum Composite...
- A6082 Anodized Aluminium Anode...
- aluminum honeycomb core foil
- aluminum foil for insulated fl...
- 1100 aluminum Rectangular squa...
- alu clad pipe insulation
- 6061 aluminum hex bar
- 2A14 aluminum alloy thick plat...